In recent years, plate heat exchangers are characterized by their light weight, small footprint, low investment, high heat exchange efficiency, flexible assembly, and easy scale removal. Dalam beberapa tahun terakhir, penukar panas pelat dicirikan oleh bobotnya yang ringan, tapak kecil, investasi rendah, efisiensi pertukaran panas tinggi, perakitan fleksibel, dan penghilangan skala yang mudah. It will be gradually promoted and used in crafts from all walks of life. Ini akan secara bertahap dipromosikan dan digunakan dalam kerajinan tangan dari semua lapisan masyarakat. However, due to the small cross section of the plate heat exchanger. Namun, karena penampang kecil pelat penukar panas. After scaling, blockage occurs at rest, which reduces the heat exchange efficiency of the plate heat exchanger, thereby affecting the safety of the equipment and the normal use of users. Setelah penskalaan, penyumbatan terjadi saat istirahat, yang mengurangi efisiensi penukar panas pelat penukar panas, sehingga memengaruhi keamanan peralatan dan penggunaan normal pengguna. therefore. karena itu. Solve the cleaning of the plate heat exchanger to prevent the formation of scale. Memecahkan pembersihan penukar panas piring untuk mencegah pembentukan skala. It will become an important issue to ensure safe production and economic operation. Ini akan menjadi masalah penting untuk memastikan produksi yang aman dan operasi ekonomi.
Plate heat exchanger in use. Penukar panas piring sedang digunakan. Due to improper operation of water treatment equipment. Karena pengoperasian peralatan pengolahan air yang tidak tepat. Water quality control is not up to standard, unqualified demineralized water is injected into the system, so that calcium, magnesium and carbonate in the water will decompose into calcium carbonate and magnesium hydroxide precipitation Kontrol kualitas air tidak memenuhi standar, air demineralisasi yang tidak memenuhi syarat disuntikkan ke dalam sistem, sehingga kalsium, magnesium, dan karbonat dalam air akan terurai menjadi kalsium karbonat dan pengendapan magnesium hidroksida
Knots on the heated surface of the heat exchanger, forming a hard scale. Simpul pada permukaan yang dipanaskan dari penukar panas, membentuk skala yang keras. Due to the poor thermal conductivity of scale, the heat exchange efficiency of the heat exchanger is reduced and the thermal energy is wasted. Karena konduktivitas termal skala yang buruk, efisiensi pertukaran panas dari penukar panas berkurang dan energi panas terbuang. Thus affecting the effect of heat transfer. Sehingga mempengaruhi efek perpindahan panas.
Metode pembersihan fouling penukar panas pelat
Pilihan agen pembersih
The choice of cleaning agent is currently pickling, which includes organic acids and inorganic acids. Pilihan agen pembersih saat ini adalah pengawetan, yang meliputi asam organik dan asam anorganik. Organic acids mainly include: oxalic acid, formic acid and so on. Asam organik terutama meliputi: asam oksalat, asam format dan sebagainya. Inorganic acids mainly include hydrochloric acid and nitric acid. Asam anorganik terutama meliputi asam klorida dan asam nitrat. According to the analysis of heat exchanger fouling and process, material and scale composition: Menurut analisis pengotoran dan proses penukar panas, komposisi bahan dan skala:
The heat exchanger has a small circulation area and a complicated internal structure. Penukar panas memiliki area sirkulasi kecil dan struktur internal yang rumit. If the cleaning liquid is precipitated, it is not easy to discharge. Jika cairan pembersih diendapkan, tidak mudah untuk dibuang.
The heat exchanger is made of nickel-titanium alloy, using hydrochloric acid as the cleaning fluid. Penukar panas terbuat dari paduan nikel-titanium, menggunakan asam klorida sebagai cairan pembersih. Idleness will cause strong corrosion to the plates and shorten the service life of the heat exchanger. Kemalasan akan menyebabkan korosi yang kuat pada pelat dan mempersingkat masa pakai penukar panas.
Through repeated experiments, it was found that formic acid was the best choice for cleaning solution. Melalui percobaan berulang, ditemukan bahwa asam format adalah pilihan terbaik untuk larutan pembersih. Adding buffers and surfactants to the formic acid cleaning solution improves the cleaning effect and reduces the corrosion of the cleaning solution to the plates. Menambahkan buffer dan surfaktan ke larutan pembersih asam format meningkatkan efek pembersihan dan mengurangi korosi larutan pembersih ke pelat. The chemical test research on the scale samples shows that formic acid can effectively remove the scale. Penelitian uji kimia pada sampel skala menunjukkan bahwa asam format dapat secara efektif menghilangkan timbangan. Through the acid immersion test, it was found that formic acid can effectively remove the scale attached to the plate, and its corrosion effect on the heat exchanger plate is also very small. Melalui tes perendaman asam, ditemukan bahwa asam format dapat secara efektif menghilangkan skala yang melekat pada pelat, dan efek korosinya pada pelat penukar panas juga sangat kecil.

Prinsip dasar menghilangkan skala
Solusi: larutan asam bereaksi dengan skala kalsium, magnesium dan karbonat untuk menghasilkan senyawa yang larut dan skala larut.
Peeling effect: acid solution can dissolve oxides on the metal surface. Efek mengupas: larutan asam dapat melarutkan oksida pada permukaan logam. Destroy the combination with scale. Hancurkan kombinasi dengan skala. As a result, scale adhering to the surface of the metal oxide is peeled off. Akibatnya, skala yang menempel pada permukaan oksida logam terkelupas. And fall off. Dan jatuh.
Gas lift function: After the acid solution reacts with calcium, magnesium and carbonate scale, a large amount of carbon dioxide is produced. Fungsi pengangkatan gas: Setelah larutan asam bereaksi dengan skala kalsium, magnesium, dan karbonat, sejumlah besar karbon dioksida dihasilkan. Carbon dioxide gas is overflowing. Gas karbon dioksida meluap. For the insoluble or slow-dissolving scale layer, it has a certain lifting power to make the scale fall off from the heated surface of the heat exchanger. Untuk lapisan skala yang tidak larut atau larut lambat, ia memiliki daya angkat tertentu untuk membuat skala jatuh dari permukaan yang dipanaskan dari penukar panas.
Efek melonggarkan: Untuk skala yang mengandung silikat dan sulfat, karena oksida kalsium, magnesium, karbonat dan besi larut dalam larutan asam, skala yang tersisa akan menjadi longgar, menunggu untuk hanyut oleh larutan asam yang mengalir.
Langkah-langkah untuk mencegah pengotoran penukar panas piring
Strictly control the water quality during the operation. Kontrol kualitas air dengan ketat selama operasi. The water in the system and the softened water in the softening tank must be subjected to strict water quality tests before they can be injected into the pipe network. Air dalam sistem dan air lunak dalam tangki pelunakan harus dikenai tes kualitas air yang ketat sebelum dapat disuntikkan ke jaringan pipa.
When the new system is put into operation, the heat exchanger should be separated from the system, and after a period of circulation, the heat exchanger should be integrated into the system. Ketika sistem baru dioperasikan, penukar panas harus dipisahkan dari sistem, dan setelah periode sirkulasi, penukar panas harus diintegrasikan ke dalam sistem. In order to avoid impurities in the pipe network into the heat exchanger. Untuk menghindari kotoran di jaringan pipa ke penukar panas.
Di seluruh sistem, selain pembersihan yang tidak teratur pada filter kotoran dan filter, jaringan pipa juga harus dijaga kebersihannya agar penukar panas tidak terhalang.